 abstract={The paper presents the results of comparative tests of the fatigue properties conducted on two non-ferrous alloys designated as Al 6082 and Al 7075 which, due to the satisfactory functional characteristics, are widely used as engineering materials. The fatigue tests were carried out using a proprietary, modified low cycle test (MLCF). Particular attention was paid to the fatigue strength exponent b and fatigue ductility exponent c. Based on the tests carried out, the results comprised within the range defined by the literature were obtained. These results prove a satisfactory sensitivity of the method applied, its efficiency, the possibility of conducting tests in a fully economical way and above all the reliability of the obtained results of the measurements. Thus, the thesis has been justified that the modified low cycle fatigue test (MLCF) can be recommended as a tool used in the development of alloy characteristics within the range of low-cycle variable loads},
 type={Artykuły / Articles},
 title={Characteristics of Non-Ferrous Metal Alloys as Determined by Low-Cycle Fatigue Test under Variable Loads},
 URL={http://www.journals.pan.pl/Content/87853/PDF/17_paper.pdf},
 doi={10.2478/afe-2014-0017},
 keywords={Fatigue resistance, Low-cycle fatigue test (LCF), Material constants},
}