TY - JOUR N2 - Hot Isostatic Pressing elaboration of Norem02, an austenitic-ferritic hypereutectoid stainless steel, leads to the formation of an austenitic matrix with a mixture of acicular M7C3 and globular M23C6 carbides. The sintering tests, carried out by using an AISI 304L container, showed that the final microstructure and the carbides’ distribution of the HIPed Norem02 are strongly influenced by the process parameters (heating and cooling rate, sintering time, holding temperature and pressure) and by the particles’ size, microstructure and phase distribution of the initial powder. The morphological, crystallographic and chemical analysis of the sintered samples were completed by comprehension of the diffusion phenomena at the Norem02/304L interface, enabling the establishment of a correlation between elaboration process and final microstructure. L1 - http://www.journals.pan.pl/Content/110128/PDF/AMM-2019-1-06-Tellier.pdf L2 - http://www.journals.pan.pl/Content/110128 PY - 2019 IS - No 1 EP - 38 DO - 10.24425/amm.2019.126215 KW - powder metallurgy KW - hot isostatic pressing KW - high carbon steel KW - microstructure KW - hardfacing coating A1 - Tellier, A. A1 - Ardigo-Besnard, M.R. A1 - Chateau-Cornu, J.-P. PB - Institute of Metallurgy and Materials Science of Polish Academy of Sciences PB - Committee of Materials Engineering and Metallurgy of Polish Academy of Sciences VL - vol. 64 DA - 2019.03.14 T1 - Influence of the process parameters on the microstructure of a hardfacing coating elaboratedby hot isostatic pressing SP - 33 UR - http://www.journals.pan.pl/dlibra/publication/edition/110128 T2 - Archives of Metallurgy and Materials ER -