TY - JOUR N2 - The production process of prosthetic restorations runs in two stages. In the first stage, the prosthetic foundation is produced of metal alloys. In the second stage, a facing material is applied on the produced element. In both stages, the wettability is significantly important, as well as the free surface energy relating to it. The quality of the obtained cast depends on the surface phenomena occurring between the metal alloy and the material of which the casting mould is made. The performed examinations also point to a relation between the ceramics joint and the base, depending on the wetting angle. The aim of the presented paper was to examine influence of the composition of a Ti(C,N)-type coating on bases made of the Ni-Cr prosthetic alloy on the wettability and the surface free energy. The test material were disks made of the Ni-Cr alloy with the diameter of 8 mm. The disks were divided into five groups, which were covered with Ti(C,N) coatings, with different amounts of C and N in the layer. In order to determine the surface free energy (����), the wetting angle was measured. Two measure liquids were applied: distilled water and diiodomethane. The obtained results of the measurements of the water-wetting angles suggest that together with the increase of the ratio of nitrogen to carbon in the Ti(C,N) coating, the surface hydrophobicity increases as well. In all the samples, one can see a large difference between the energy values of the polar and the apolar components. The high values of the polar components and the low values of the apolar ones make it possible to conclude that these surfaces exhibit a greater affinity to the polar groups than to the apolar ones. On the basis of the analysis of the surface free energy, one can state that covering the alloy with Ti(C,N)-type coatings should not decrease the adhesion of the ceramics to the alloy, whereas TiC coatings should lead to the latter’s improvement. Due to their hydrophilicity, TiC coatings should decrease the adhesion of bacteria to the surface and hinder the formation of a bacterial biofilm. L1 - http://www.journals.pan.pl/Content/88633/PDF/02_paper.pdf L2 - http://www.journals.pan.pl/Content/88633 PY - 2015 IS - No 3 DO - 10.1515/afe-2015-0050 KW - Dental alloys KW - Wettability KW - Contact angle KW - Surface tension KW - Surface free energ A1 - Banaszek, K. A1 - Klimek, L. PB - The Katowice Branch of the Polish Academy of Sciences DA - 2015[2015.01.01 AD - 2015.12.31 AD] T1 - Wettability and Surface Free Energy of Ti(C,N) Coatings on Nickel-based Casting Prosthetic Alloys UR - http://www.journals.pan.pl/dlibra/publication/edition/88633 T2 - Archives of Foundry Engineering ER -