MoO3 thick film was manufactured by using a thermal spray process (Atmospheric Plasma Spray, or APS) and its microstructure, phase composition and properties of the coating layer were investigated. Initial powder feedstock was composed of an orthorhombic α-MoO3 phase, and the average powder particle size was 6.7 μm. As a result of the APS coating process, a MoO3 coating layer with a thickness of about 90 μm was obtained. Phase transformation occurred during the process, and the coating layer consisted of not only α-MoO3 but also β-MoO3, MoO2. Phase transformation could be due to the rapid cooling that occurred during the process. The properties of the coating layer were evaluated using a nano indentation test. Hardness and reduced modulus were obtained as 0.47 GPa and 1.4 GPa, respectively. Based on the above results, the possibility of manufacturing a MoO3 thick coating layer using thermal spray is presented.

Co-Cr-Mo based sheet I-WP lattice was fabricated via laser powder bed fusion. The effect of microstructure and the I-WP shape on compressive mechanical response was investigated. Results of compression test showed that yield strength of the sheet I-WP was 176.3 MPa and that of bulk Co-Cr-Mo (reference material) was 810.4 MPa. By applying Gibson-Ashby analytical model, the yield strength of the lattice was reversely estimated from that of the bulk specimen. The calculated strength of the lattice obtained was 150.7 MPa. The shape of deformed lattice showed collective failure mode, and its microstructure showed that strain-induced martensitic transformation occurred in the overall lattice. The deformation behavior of additively manufactured sheet I-WP lattice was also discussed.