Sodium orthovanadate was tested as a corrosion inhibitor of intermetallic Al2Cu in 1 M H3PO4. The Al2Cu – H3PO4 – Na3VO4 system was studied using the following methods: inductively coupled plasma optical emission spectrometry, scanning electron microscopy with energy dispersive x-ray spectroscopy, x-ray diffraction, electrochemical impedance spectroscopy, polarisation and open circuit potential. It was found that the corrosion rate decreased as the inhibitor concentration increased. The highest inhibition efficiency 99% was obtained when sodium orthovanadate initial concentration was equal to 100 mM, pH = 1.11, due to precipitation of a protective layer of insoluble salt, containing vanadium, phosphorus, sodium and oxygen, on the surface. At pH = 0.76 the protective layer was not formed and inhibition efficiency decreased to 76%. Selective corrosion of the intermetallic phase caused a significant increase of an electric double layer capacitance and decrease of a charge transfer resistance.

Opisano podstawy chemiczne jednego z wariantów chelatowej metody usuwania tlenków siarki i azotu z gazów odlotowych. Szczególną uwagę zwrócono na reakcje chemiczne prowadzące do powstawania odpadów stałych. Przedstawiono schemat technologiczny oraz omówiono działanie przemysłowej instalacji usuwania SO2, NOx i pyłu ze spalin z dwóch kotłów rusztowych o mocy 29 MW, każdy. Dokonano bilansu materiałowego procesu oczyszczania gazów i na tej podstawie określono ilość odpadów stałych powstałych podczas 3-tygodniowych testów eksploatacyjnych technologii.