The paper presents the results of research on microstructure and impact strength of AlSi13Cu2 matrix composite reinforced by Ni-coating carbon fibers (CF) with a volume fraction of 5%, 10% and 15%. The composite suspensions were prepared using by stirring method and subsequently squeeze casted under different pressures of 25, 50, 75 and 100 MPa. As part of the study, fiber distribution in aluminum matrix was evaluated and variation in impact strength of composite as a function of the carbon fibers volume fraction and pressure applied were determined. It has been found that the presence of Ni coating on carbon fibers clearly improves their wettability by liquid aluminum alloy and in combination with the stirring parameters applied, composite material with relatively homogeneous structure can be produced. Charpy's test showed that the impact strength of composite reaches the highest value by carrying out the squeeze casting process at 75 MPa. In the next stage of research, it was found that the impact strength of composites increases with the increase of carbon fibers volume fraction and for 15% of fibers is close to 8 J/cm2. Observations of fracture surfaces have revealed that crack growth in the composites propagates with a quasi-cleavage mechanism. During the creation of the fracture, all fibers arranged perpendicular to its surface were sheared. At the same time, the metal matrix around the fibers deformed plastically creating characteristic ductile breaks. The fracture surface formation through the fibers indicates a cohesive and strong connection of the reinforcement with the matrix. In addition to the phenomena mentioned, debonding the fiber-matrix interfaces and the formation of voids between components were observed on the fracture surface.
The paper presents the results of investigations concerning the influence of gray cast iron modification on free vibration frequency of the disc casting. Three different chemical composition melts of gray cast iron were prepared in induction furnace. During gravity casting 0.05% and 0.3% mass of the Inolate modifier was added on stream of metal for changing graphite flakes in castings. Sound signal vibration of cast iron sample was registered by means on microphone for free vibration frequency measurements. Decreasing of free vibration frequency of modified cast iron in comparison with non modified castings was observed. Higher contents of modifier causes more decreasing of free vibration frequency. Cast iron with smaller contents of carbon and silicon have higher free vibration frequency in comparison with eutectic composition cast iron. Hardness of examined cast iron is lower when the more modifier is added during modification process. Free frequency is smaller with smaller Brinell hardness of disc casting. It was concluded that control of free vibration frequency of disc castings by means of chemical composition and modification process can improved comfort and safety of working parts.