The purpose of the paper was to design geometric models of the movable connection made of brass for three different attachment options and three different loads. The numerical analysis of the mechanical properties, stresses, strains and displacements using the finite element method was carried out in SolidWorks 2020 and their comparative analysis was performed. The computer simulations performed will allow the boundary conditions that directly affect the mechanical properties of the engineering materials to be optimised.

In Eurocode 5, the stiffness equation for bolted steel-wood-steel is stated as a function ofwood density and fastener diameter only. In this research, an experimental study on various configurations of tested bolted steel-wood-steel (SWS) connections has been undertaken to predict the initial stiffness of each connection. In order to validate the Eurocode 5 stiffness equation, tests on 50 timber specimens (40 glued laminated timbers and 10 laminated veneer lumbers (LVL)) with steel plates were undertaken. The number of bolts was kept similar and the connector diameter, timber thickness, and wood density were varied. The results obtained in the experimental tests are compared with those obtained from the Eurocode 5 stiffness equation. From the analysis, it is signified that the stiffness equation specified in Eurocode 5 for bolted SWS connections does not adequately predict the initial stiffness. The results from Eurocode 5 stiffness equation are very far from the experimental values. The ratio of stiffness equation to experimental results ranges from 3.48 to 4.20, with the average at 3.77, where the equation overpredicted the experimental stiffness value for the connection. There is a need to consider or incorporated other parameters such as geometric configurations in Eurocode 5 stiffness equation to improve the ratio with the experimental data.

Foamed concrete incorporating processed spent bleaching earth (PSBE) produces environmentally friendly foamed concrete. Compressive strength, porosity, and rapid chloride penetration tests were performed to investigate the potential application for building material due to its low density and porous concrete. Laboratory results show that 30% PSBE as cement replacement in foamed concrete produced higher compressive strength. Meanwhile, the porosity of the specimen produced by 30% PSBE was 45% lower than control foamed concrete. The porosity of foamed concrete incorporating PSBE decreases due to the fineness of PSBE that reduces the volume of void space between cement and fine aggregate. It was effectively blocking the pore and enhances the durability. Consistently, the positive effect of incorporating of PSBE has decreased the rapid chloride ion permeability compared to that control foamed concrete. According to ASTM C1202-19 the foamed concrete containing 30% PSBE was considered low moderate permeability based on its charge coulombs value of less than 4000. Besides, the high chloride ion permeability in foamed concrete is because the current quickly passes through the specimen due to its larger air volume. In conclusion, incorporating PSBE in foamed concrete generates an excellent pozzolanic effect, producing more calcium silicate hydrate and denser foamed concrete, making it greater, fewer voids, and higher resistance to chloride penetration.

Porous asphalt mixture (PA), known as open-graded surfaces over a stone bed underneath, allows water to go through. These factors can affect the porous asphalt mixture adhesive strength. The high amount of course aggregate promotes the structure of air voids have certain impacts on the acoustic properties of porous asphalt. The materials properties are consisting of both aggregate and bitumen tests. This study also details out the aggregates sieve analysis test to develop new aggregate gradation for PA. According to five ASEAN countries’ specifications, the sieve analysis test was done. The countries included are Malaysia, Vietnam, Thailand, Singapore, and Indonesia. The test for the binder includes the softening point, penetration, and ductility. This study also investigates the addition of kenaf fiber in the mixture as an additive. Mechanical performance test for PA using Marshall Stability test to identify the strength and the properties of the conventional PA with the addition of kenaf fiber compared to the new gradation of PA incorporating kenaf fiber. From the results, the addition of 0.3% kenaf modified PA improved the performance of PA in terms of Marshall Stability and volumetric properties.

Due to urbanization, the population in the major cities in Malaysia is approximately 72.8% of its total population. The increase of population density has directly increased the amount of sewerage sludge waste that poses threat to the environment. In line with the green initiatives, alternative method to develop good quality concrete material from sewerage sludge waste can be further explored. Traditionally, sewerage sludge waste is processed using incinerator that require high energy and it is time consuming. In this study, microwave heating which require less energy consumption and less time consuming is used for sewerage sludge preparation. Prior to heating process, sewerage sludge waste is over dried at 105°C for 24 hours. Three types of microwave heating namely medium heating, medium high heating and high heating has been used. The chemical and physical properties microwaved sewerage sludge ash (MSSA) was tested using X-Ray Fluorescence (XRF), X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). Based on the result, the recommended temperature for the MSSA production for the concrete is High Mode Temperature. This is due to the result of MSSA for X-Ray Fluorescent test as its shows the highest in the content for pozzolanic element which are SiO2 and Fe2O3 that produce after the microwave burning process. The mineralogical composition and the crystalline phase of the High temperature MSSA due to X-Ray Diffraction test also shows high content of SiO2 as the major component as it is good for pozzolanic reaction in concrete. From the Scanning Electron Microscope test, it is observed that particle of High heated MSSAare slightly smaller than other temperature. Also, the densification occurs at High temperature MSSA. Hence, the optimal burning temperature mode for MSSA is High Mode temperature.

Malaysia’s construction industry is experiencing rapid growth, translating into increased demand for cement. However, cement production pollutes the air to the detriment of the climate via CO2 emission, making research into a cementitious replacement in concrete a necessity. This paper details an experimental study of self-compacting concrete (SCC) with partial replacement of cement by rice straw ash (RSA), which is expected to result in environmental preservation due to the green materials being used in cement production. The physicomechanical properties of the SCC with RSA replacement were determined via its compressive strength, water absorption, self-workability, and fire resistance (residual strength after exposure to high temperatures). The proportion of RSA replacement used were 0%, 5%, 10%, 15%, 20%, and 25%, and all passed the slump flow test, except the 20% and 25% samples. The SCC samples with 15% of RSA replacement reported the highest compressive strength at 7 and 28 curing days and the highest residual strength post-exposure to high temperatures. The lowest percentage of water absorption was reported by the 15% of RSA replacement, with a density of 2370 kg/m3.

Low calcium fly ash is used as the main material in the mixture and the crumb rubber was used in replacing fine aggregates in geopolymer mortar. Sodium hydroxide (NaOH) and sodium silicate (Na2SiO3) which were high alkaline solution were incorporated as the alkaline solution. The fly ash reacted with the alkaline solution forming alumino-silicate gel that binds the aggregate to produce a geopolymer mortar. The loading of crumb rubber in the fly ash based geopolymer mortar was set at 0% (CRGM-0), 5% (CRGM-5), 10% (CRGM-10), 15% (CRGM-15), and 20% (CRGM-20), respectively. NaOH solution (12M) and Na2SiO3 solution ratio is set constant at 2.5 for all geopolymer mixture and the fly ash to alkali activator ratio was kept at 2.0. The CRGM at 28 days of curing time was exposed to elevated temperature at 200°C, 400°C, 600°C and 800°C. The weight loss of the CRGM increases with increasing temperature at all elevated temperatures. However, the density and compressive strength of CRGM decrease with an increase of crumb rubber loading for all elevated temperature exposure. The compressive strength of CRGM reduced due to the fact that rubber decomposes between 200°C and 600°C thereby creating voids. CRGM-15 and CRGM-20 showed cracks developed with rough surface at 800°C. Image obtained from scanning electron microscope (SEM) showed that, the CRGM changed significantly due to the decomposition of crumb rubber and evaporation of the free water at 400°C, 600°C and 800°C.