Copper-based alloys with the addition of Al present excellent properties and can be considered a proper choice for applications as contact materials based on their good strength and fret resistance. Cu-Al alloys are used in different systems parts as bearings, gears and worm gears. The intention is to replace steel materials with new copper-based materials for parts that work in a possible explosive environment to reduce the possibility of spark appearance. Copper-berilyum alloys are known as non-sparking alloys and are used in different tools obtaining for environments with possible explosive gaseous. Results from the obtaining and analysis of a new alloy based on CuAlBe are given. The material was melted in a vacuum induction furnace from CuBe master alloy and high purity aluminium and cast into a metallic die. The alloys obtained were analyzed using EDS – energy dispersive spectroscopy for chemical composition, OM-optical and SEM-electronic microscopy for the microstructure, and the electro-corrosion resistance was tested using linear Tafel diagram and cyclic potentiometry.

The Fe-based alloy with manganese led to the appearance of new austenitic alloys, with the antiferromagnetic property pursued, resulting in compatibility with the magnetic field as that of magnetic resonance imaging. The corrosion resistance behavior of the biodegradable Fe-Mn-Si alloy was analyzed in a thermostatic chamber at 37±1°C for 24, 48 and 72 hours by immersing in Ringer solution. Also, the cast and laminated samples were subjected to electro-corrosion tests using a potentiostat equipment. Linear and cyclic potentiometry is presented for characterize the corrosion behavior of the experimental samples in electrolyte. Due to the interaction between the alloy and the liquid medium a change in the solution pH was observed. Structure analysis and chemical composition details of the surfaces were obtained using electron scanning microscopy (SEM) and X-ray energy dispersive spectroscopy (EDS).