The properties of expansive concretes made of two types of cement: Portland cement CEM I and blast furnace slag cement CEM III were tested. The expansion of the concrete was caused by using an expansive admixture containing aluminium powder added in an amount of 0.5; 1 and 1.5% of cement mass. It was found that the compressive strength of concrete with CEM I decreased after using an expansive admixture in the amount of more than 0.5% of the cement mass. The compressive strength of concrete with CEM III decrease after addition of admixture in the entire range of dosages used. On the basis of electrochemical measurements, it was found no influence of an expansive admixture on corrosion of reinforcing steel. The use of an expansive admixture causes a slight increase in the effective diffusion coefficient of chloride ions in concrete.

In the recent years a tendency for design of increasingly slender structures with the use of high performance concrete has been observed. Moreover, the use of high performance concrete in tunnel structures, subject to high loads with possibility of extreme loads occurrence such as fire, has an increasing significance. Presented studies aimed at improving high performance concrete properties in high temperature conditions (close to fire conditions) by aeration process, and determining high temperature impact on the concretes features related to their durability. In this paper it has been proven that it is possible to obtain high performance concretes resistant to high temperatures, and additionally that modification of the concrete mix with aerating additive does not result in deterioration of concrete properties when subject to water impact in various form.