Polycrystalline samples BaTiO3 and the solid solutions Ba0.9Sr0.1TiO3, Ba0.9Sr0.1Ti0.9Sn0.1O3, Ba0.9Sr0.1Ti0.8Sn0.2O3 were obtained by means of a mechanochemical treatment based on the high-energy ball milling technique and next a high temperature solid state reaction method. The influence of synthesis condition on microstructural, dielectric and ferroelectric properties of obtained solid solutions were investigated. The structure and morphology of the investigated samples were characterized by an X-ray diffraction (XRD) and scanning electron microscopy (SEM). The characterization of electrical properties of the ceramics within the temperature range from –130°C to 250°C were performed by means of a dielectric spectroscopy method at the frequency ranging from 0.1 Hz to 10 MHz. The diffusion of the paraelectric – ferroelectric phase transition and dielectric relaxation for ceramic samples are described.
This paper presents the results of obtaining and investigations of Pb1–xBax(Zr1–yTiy)1–zSnzO3 (PBZTS) ceramics with constant x = 0.03 and y = 0.02, and variable z = 0, 0.04, 0.06 and 0.08 (abbreviations of the samples were following PBZTS0, PBZTS4, PBZTS6, PBZTS8, respectively). The investigated compositions are close to rhombohedral-orthorhombic morphotropic phase boundary. The ceramic samples have been obtained by conventional ceramic technology from simple oxides PbO, ZrO2, TiO2, SnO2 and barium carbonate BaCO3. The ceramic powders, after calcination, have been pressed into discs and sintered using free sintering (FS) method. For samples obtained in such a way, the dielectric properties at various frequencies and electrical conductivity have been investigated. The increase of Sn content orders the microstructure of ceramics, and as a result the improvement of the dielectric properties of ceramic samples can be obtained.
This paper discusses the influence of the direction of applied deformation on the ability to gelation of thermosensitive chitosan hydrogels. The application of the shear rate equal in value to the classically performed oscillatory measurements leads to significantly different shapes of experimental curves. It was found that the type of mechanically applied deformation has a significant impact on the gelation ability of colloidal chitosan solutions and conditions of sol-gel phase transition. Simple shear leads to a phase transition at a lower temperature or in a shorter time compared to oscillatory tests. Moreover, based on the final values of dynamic viscosity in rotational measurements, it was found that stronger crosslinking of the polymer structure was observed.
TiNi alloys have excellent shape memory properties and corrosion resistance as well as high biocompatibility. This study investigated the effects of copper addition on the phase transitions and electrochemical corrosion behaviors of Ti50Ni50-xCux alloys. TiNi, Ti50Ni47Cu3, Ti50Ni44Cu6, and Ti50Ni41Cu9 alloys were prepared using vacuum arc remelting followed by 4 h homogenization at 950°C. Differential scanning calorimetry and X-ray diffraction analyses were conducted. The corrosion behaviors of the alloys were evaluated using potentiodynamic polarization test in Hank’s balanced salt solution at a temperature of 36.5 ± 1°C. The TiNi alloy showed phase transitions from the cubic B2 phase to the monoclinic B19’ phase when the alloy was thermally cycled. The addition of copper to the TiNi alloy played a major role in stabilizing the orthorhombic B19 phases during the phase transitions of Ti50Ni50-xCux alloys. The shifts in the corrosion potential toward the positive zone and the low corrosion current density were affected by the amount of Cu added. The corrosion resistance of the TiNi alloy increased with increasing copper content.